Kuczynska H.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Linger E.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Waskiewicz S.,Silesian University of Technology
Przemysl Chemiczny | Year: 2012

Five com. acrylic resins were mixed in varying proportions to binary mixts., diluted with a mixed solvent, optionally pigmented with Al flake paste, formed as coatings on glass and steel substrates and studied for surface tension, solubility parameter, stratification degree (phase sepn.), microstructure of crossections, hardness, adhesion to the substrates, as well as bending and impact strengths. Some pairs of acrylic resins were capable of phase sepn. and migration of sepd. phases to the air/coating or coating/substrate interfaces. The pigmentation of the upper layer with Al flakes resulted in formation of the coating systems with decorative properties and excellent adhesion to steel.


Kiedik M.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Kubica S.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Hreczuch W.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Basta A.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach
Przemysl Chemiczny | Year: 2012

Fundamentals and development of the Polish process for prodn. of (p-HOC6H4)2 CMe2 were presented.


Langer E.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Kaminska-Bach G.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Kaminska-Tarnawska E.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach
Przemysl Chemiczny | Year: 2012

Six inorg. pigments were studied for Flory-Huggins and solubility parameters in 15 org. solvents by inverse gas chromatogr. and sedimentation methods. The detd. values were tabulated.


Gibas E.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Rymarz G.,Oddzial Zamiejscowy Farb i Tworzyw w Gliwicach | Cichy B.,Instytut Nawozow Sztucznych | Kuzdzal E.,Instytut Nawozow Sztucznych | Turkowska M.,Instytut Nawozow Sztucznych
Przemysl Chemiczny | Year: 2012

Fe(III) and Mn(II) stearates were added to low-d. polyethylene films to increase their degradability under atm. conditions and UV irradn. The addn. resulted in a decrease in mol. mass, tensile strength and elongation at break of the polymer and in an increase of the carbonyl index and microbial degrdn. rate.